每周分享:An acid-free route for the facile synthesis of iron-functionalized mesoporous silicas: Transformation between hollow nanospheres and cage-like mesostructures 

今天給大家分享的是2014年5月份 《Microporous and Mesoporous Materials》上發表的一篇名為:An acid-free route for the facile synthesis of iron-functionalized mesoporous silicas: Transformation between hollow nanospheres and cage-like mesostructures

文章摘要如下:

Iron-substituted silicas with hollow nanospherical morphology and cage-like mesostructure have been synthesized using triblock copolymer F127 as surfactant and tetramethoxysilane (TMOS) as silica source with no necessary addition of mineral acids. Iron-functionalized hollow nanospheres were obtained using Fe(acac)3 as iron source. When Fe(NO3)3 was employed as iron source, iron-containing cage-like FDU-12 mesostructure and hollow nanospheres were formed with Fe/Si molar ratio lower than 0.008 and higher than 0.015, respectively. The formation of hollow spheres at high Fe/Si ratio can be regarded as gradually dissociation of nanocages from Fe-FDU-12. The structure of the iron centers was determined by spectroscopic methods (UV–vis and UV–Raman measurements) and by elemental analyses. The facile structural evolution between cage-like and nanospherical structures may be helpful for further understanding the formation mechanism of mesoporous silicas.

該文章中材料表征采用的是美國麥克儀器AutoChem 2920

詳情可參考下面鏈接:

http://www.sciencedirect.com/science/article/pii/S1387181114000456